Metallographic analysis sample preparation is the key! Especially for the samples with irregular shape and small size, which cannot be directly clamped by the fixture for grinding and polishing, they become the samples with standard shape and size after inlay, which makes it easy for manual polishing and automatic polishing. Inlay is divided into cold inlay and hot inlay. Whether it is cold or hot inlay, it is very important to select the appropriate inlay consumables. Based on years of work practice, the editor believes that imported consumables can be used for metallographic sample inlay with high requirements. Qmaxis' metallographic inlay series products are a very good choice. Cold and hot inlay consumables are complete, which can meet the metallographic inlay requirements of various materials.


Cold mounting material

Qmaxis metallographic cold inlay special epoxy resin, acrylic resin and curing agent are suitable for inlay of materials sensitive to temperature and pressure.


Epoxy resin and curing agent have good physical adsorption capacity, low shrinkage, can penetrate into the pores and cracks of the sample, and are closely combined with the sample after curing, with good edge retention, so they are widely used.


--Epoquick epoxy resin and curing agent series, 2h/room temperature


--Epocure epoxy resin and curing agent series, 6h/room temperature


Acrylic resin and curing agent, with short curing time and low cost, are more suitable for rapid sample preparation and are still widely used.


--Acryquick acrylic resin and curing agent series, 8-12min/room temperature


With qmaxis metallographic cold inlay material, rapid inlay of metallographic samples can be easily realized. The only standard is practical inspection. Qmaxis testing Nanjing laboratory can operate it by hand. Welcome to contact qmaxis testing engineers and visit qmaxis testing laboratory in Nanjing for free trial.


Thermal mosaic material

Qmaxis metallographic hot mosaic special hot pressing mosaic powder is suitable for the mosaic of materials that can withstand a certain temperature and pressure. The edge is kept very good, the resin is very stable, and will not be affected by heating or corrosive agents. Therefore, these hot mosaic materials are usually used for temperature and pressure resistant materials.


Phenolic resin phenopowder, black/red, for inlay of low hardness materials


Epoxy resin epowder g (particle)/epowder f (powder), black, suitable for high hardness material inlay, with excellent edge retention. G-type granules are relatively easy to clean. F-type powder is relatively more suitable for sample inlay with complex geometry.


Acrylic resin transpowder is transparent after curing and suitable for visible sample inlay.


Conductive filler copper conductive filler/graphpowder carbon conductive filler for SEM and TEM analysis. Copperpowder copper conductive filler is used for sample inlay without analyzing copper, and graphpowder carbon conductive filler is used for sample inlay without analyzing carbon.


With qmaxis metallographic thermal inlay material, it is easy to inlay high-quality samples with good edge preservation. The only standard is practical test, which can be operated by Nanjing Laboratory of pulse detection. Welcome to contact pulse testing engineers and visit the pulse testing laboratory in Nanjing for free trial.


Inlay auxiliary consumables

Qmaxis inlay auxiliary materials are available in all kinds of molds, sample fixing clips, mixed wax paper cups, stirring rods, mold release agents, glass slides and other auxiliary consumables in the process of metallographic sample inlay. All from the United States can be imported with original packaging, which is cheap.


The only standard is practical test, which can be operated by Nanjing Laboratory of pulse detection. Welcome to contact pulse testing engineers and visit the pulse testing laboratory in Nanjing for free trial.


Metallographic mosaic machine

The metlab series metallographic inlay machines of comer in the United States have been used for more than 50 years. These metallographic inlay machines are famous for their economy and durability. High cost performance is its core competitiveness. Cold inlaid vacuum permeameter; There is a full-automatic hot press inlay machine. The single cylinder hot press inlay machine can inlay two samples at a time, and the double cylinder hot press inlay machine can inlay four samples at a time. The whole process only takes 8min. It is fully automatic and programmable. These devices are safe and reliable, pay attention to details, and are ideal inlay equipment for metallographic laboratory.

Qmaxis metallographic inlay series products are not only very easy to use cold inlay materials, hot inlay materials and inlay auxiliary materials, but also very powerful metallographic inlay machine. Close your eyes and choose, everything is easy to use! With the pulse of metallographic inlay series products, cold and hot inlays can be easily done!


The only standard is practical test, which can be operated by Nanjing Laboratory of pulse detection. Welcome to the laboratory of pulse detection in Nanjing for free trial. Kemei's engineers are dedicated to providing you with relevant services. Please contact us immediately.